Photoinitiator FMT

Chemical Name: 

Bis(.eta.5-2,4-cyclopentadien-1-yl)-bis[2,6-difluoro-3-(1H-pyrrol-1-yl)-phenyl] titanium

CAS No.: 125051-32-3

Formula: C₃₀H₂₂N₂F₄Ti

Formula Weight: 534.37

Chemical Structure:

Appearance: yellow to orange powder
Melting Point: 165-170 ℃
Purity: 99.0%min
Volatility: 0.5%Max

FMT UV absorption spectra

Photoinitiator FMT Introduction

Character and Application:

 FMT is a kind of high-end UV and visible light photoinitiator with the same molecular structure as of the Ciba i-784 photoinitiator. It's a very reactivefree radical type curing photoinitiator.

FMT appears yellow to orange powdermelting point is at 165-170 ℃the typical absorptions are at 333nm396nm470 nmand the maximum absorption wavelength can amount to 560 nm. It's the very good UV and visible light photoinitiator which can match argon laser 488 nm emission wavelengths. Its light trigger process neither belongs to cracking typenor belongs to deprive-hydrogen typebut after it absorbs the optical energyphotoinduced heterogeneous light responding cyclo-intermediates (A)then takes place ligands replacement with oligomer and ester carbonyl of acrylate in reactive diluentproduces free radicals (B)causes polymerization and crosslinking.

  It absorbs well in visible lighthas light-decolourizatio after photolysisis very suitable for visible light curing of thick coatingcan cure coating whose thickness is above 70 μm. Its thermal decomposition temperature is at 230℃so it wouldn’t vplazmtf when boiled in or sodium hydroxide solutionfor a few hourshas excellent thermal stability.

Our FMT’s lwonderful. It can initiate as long as gived 488nm illumination of 0.8mJ/cm2 in acrylate system.

  It is mainly used in high-tec and high value-added fieldssuch as argon laser scanning curingholographic laser imagerypolyimide photocuringPCB printing inkPCB and ing dental materialsand it also can be used in UV coatingUV printing inkUV adhesivephotoresist.The usage of this product should base on the results of it can be used either individually or co-used with other photoinitiators according to the practical use conditionsand the suggested volume of addition is 0.1-5 ‰ (w/w).

Advantages:

1. Have light-decolourizatio

2. Be applicable for visible light curing of thick coating

3. Have excellent thermal stability

4. No residuumand the volume of addition is small

5. Can be used in brunet systemand the is strong

6. no pollutionno solvent evaporation

7. Photoinitiation is fast

8. The effect of Yellowing resistance is good